|There are many specialty applications within the industrial and recreational sectors. These applications include high performance automotive, insulative tapes, filtration media industrial components and sports/recreation products. Barrday’s broad base of low temperature and standard curing epoxies, BMI’s, polyesters, silicones, and other systems combined with our processing techniques has led to applications in a wide array of composite applications and markets.
Our Industrial and Recreational Solutions
Data sheet available by clicking bold link
EP145 is a low temperature curing, high performance epoxy system. Capable of curing at 145ºF (63ºC), EP145 can display Tg of 430ºF (221ºC) when suitably post cured. EP145 is designed for high performance applications that require ultra low cure temperature or co-laminating with temperature sensitive materials, such as balsa wood.
EP200 HT is an advanced epoxy prepreg system with a low temperature curing, rubber modified epoxy that offers a wide variety of curing capabilities.
EP202 is a low temperature curing, rubber modified epoxy that offers a wide variety of curing options. EP202 prepreg has the ability to snap cure at 275°F (135ºC) in a 20 minute dwell as well as cure at 170°F (77ºC) in five hours. EP202 is flame resistant and displays a Tg of 300°F+ (149ºC+) without requiring a post cure. EP202 can be used for a wide variety of structural applications.
EP254 is a low temperature curing, toughened epoxy that cures in the 235ºF to 275ºF (113 to 135ºC) range. Glass prepregs can co-laminate to carbon/epoxy prepregs without shear failure. EP254 is the most post formable composite prepreg system available today.
FA EP255SP Film Adhesive
FA EP255SP is a toughened, high peel strength, fire resistant supported film adhesive is designed for a variety of bonding applications including metal to metal, composite to core or metal to core. Sandwich constructions include can aramid, aluminum and various foams.
FA EP259 Film Adhesive
FA EP259 is a toughened, high peel strength, general purpose supported film adhesive is designed for a variety of bonding applications including metal to metal, composite to core or metal to core. Sandwich constructions include can aramid, aluminum and various foams.
EP350 is a 350ºF (177ºC) curing, modified epoxy that is self-extinguishing, passing the 60 second vertical ignition test listed in FAR 25.853. EP350 offers an excellent combination of toughness and high glass transition temperature. EP350 is capable of curing at temperatures as low as 275ºF (135ºC) and following a free standing post cure, display 356ºF (180ºC) Tg.
FM-5 is a toughened polyester system designed for table rolling applications such as fishing rods, radomes, antennae and kayak paddle shafts. It offers precisely controlled flow, excellent resistance to bending set and extremely high flexural strength making it ideal for dynamic, low frequency applications.
LC163 is a heat stable silicone prepreg system that produces prepregs with low dielectric issues.
LC909 is a high temperature curing, high performance bismaleimide system. LC909 offers outstanding mechanical properties and a very high glass transition temperature of 626ºF (330ºC).